高流動 ULTEM PEI 9066
PEI 9066 高流動性聚醚酰亞胺混合物。符合FAR 25.853和OSU 65/65標(biāo)準(zhǔn)，具有低毒性、煙霧和火焰演變。符合環(huán)保要求
High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL機械性能
|
Value | Unit | Standard |
|
Tensile Stress, yld, Type I, 5 mm/min / 抗張程度,屈服,類型I,5 mm/min
|
96
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min / 抗張程度,斷裂,類型I,5 mm/min
|
88
|
MPa
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸長,斷裂,類型I,5 mm/min
|
65
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
|
3240
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span
|
144
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 2.6 mm/min, 100 mm span
|
3170
|
MPa
|
ASTM D 790
|
|
IMPACT
|
Value | Unit | Standard |
|
Izod Impact, notched, 23°C / 懸臂梁缺口沖擊強度23°C
|
85
|
J/m
|
ASTM D 256
|
|
Izod Impact, Reverse Notched, 3.2 mm
|
1975
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Energy @ peak / 儀表控制抗沖擊能量 @ 峰值, 23°C
|
67
|
J
|
ASTM D 3763
|
|
Instrumented IMPACT Energy @ peak / 儀表控制抗沖擊能量 @ 峰值, -30
|
58
|
J
|
ASTM D 3763
|
|
THERMAL
|
Value | Unit | Standard |
|
HDT, 1.82 MPa, 6.4 mm, unannealed / 熱變形溫度，1.82 MPa, 6.4 mm, 未退火
|
195
|
°C
|
ASTM D 648
|
|
PHYSICAL
|
Value | Unit | Standard |
|
Specific Gravity/比重
|
1.28
|
–
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm / 模塑收縮量，流動，3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2 mm / 模塑收縮量，橫向，3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率, 337°C/6.6 kgf
|
11
|
g/10 min
|
ASTM D 1238
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard |
|
OSU total heat release (2 minute test)
|
10
|
kW-min/m2
|
FAR 25.853
|
|
OSU peak heat release rate (5 minute test)
|
50
|
kW/m2
|
FAR 25.853
|
|
Source GMD, last updated:01/13/2000
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature / 干燥溫度
|
135
|
°C
|
|
Drying Time / 干燥時間
|
4 – 6
|
hrs
|
|
Drying Time (Cumulative) / 干燥時間（累積的）
|
24
|
hrs
|
|
Maximum Moisture Content / 含濕量
|
0.02
|
%
|
|
Melt Temperature / 熔體溫度
|
340 – 360
|
°C
|
|
Nozzle Temperature / 注嘴溫度
|
330 – 355
|
°C
|
|
Front – Zone 3 Temperature / 前區(qū)3溫度
|
340 – 360
|
°C
|
|
Middle – Zone 2 Temperature / 中區(qū)2溫度
|
325 – 350
|
°C
|
|
Rear – Zone 1 Temperature / 后區(qū)1溫度
|
315 – 340
|
°C
|
|
Mold Temperature / 模具溫度
|
135 – 165
|
°C
|
|
Back Pressure / 背壓
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺桿速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔膠總量的百分比
|
40 – 60
|
%
|
|
Vent Depth / 排氣孔深度
|
0.025 – 0.076
|
mm
|
|
|
|
|