Tensile Stress, brk, Type I, 5 mm/min

590

kgf/cm2

ASTM D 638

Flexural Stress, brk, 1.3 mm/min, 50 mm span

1050

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

42100

kgf/cm2

ASTM D 790

Izod Impact, unnotched, 23°C

39

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

3

cm-kgf/cm

ASTM D 256

HDT, 0.45 MPa, 6.4 mm, unannealed

187

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

105

°C

ASTM D 648

CTE, -40°C to 40°C, flow

5.58E-05

1/°C

ASTM E 831

Specific Gravity

1.49

-

ASTM D 792

Mold Shrinkage, flow, 1.5-3.2 mm (5)

1.4 - 1.6

%

SABIC Method

Mold Shrinkage, flow, 3.2-4.6 mm (5)

1.5 - 1.6

%

SABIC Method

Mold Shrinkage, xflow, 1.5-3.2 mm (5)

1.3 - 1.4

%

SABIC Method

Mold Shrinkage, xflow, 3.2-4.6 mm (5)

1.4 - 1.5

%

SABIC Method

Dielectric Strength, in oil, 3.2 mm

16.9

kV/mm

ASTM D 149

Relative Permittivity, 50/60 Hz

3.1

-

ASTM D 150

Relative Permittivity, 1 MHz

2.9

-

ASTM D 150

Dissipation Factor, 50/60 Hz

0.0039

-

ASTM D 150

Dissipation Factor, 1 MHz

0.014

-

ASTM D 150